The Heat Treatment and Machinability of X6CrNi2520 Stainless Steel Grade

Химический состав:
– Carbon (C): 0.08% max
– Кремний (Si): 1.00% макс.
– Марганец (Mn): 2,00% макс.
– Фосфор (P): 0,045% макс.
– Сера (S): 0,015% макс.
– Chromium (Cr): 24.0-26.0%
– Nickel (Ni): 19.0-21.0%
– Molybdenum (Mo): 4.0-5.0%

Механические свойства:
– Tensile Strength: 620 MPa (minimum)
– Yield Strength: 260 MPa (minimum)
– Elongation at Break: 40% (minimum)
– Hardness: 95 HRB (maximum)

Термическая обработка:
X6CrNi2520 stainless steel is typically solution annealed at 1020-1100°C, followed by water quenching or rapid cooling, and then tempered at 300-350°C for 2-3 hours to achieve the desired properties.

Обрабатываемость:
X6CrNi2520 stainless steel grade exhibits good machinability when using appropriate machining techniques, such as slow speeds, heavy feeds, and sharp cutting tools. It is essential to use ample cutting fluid to reduce friction and heat generation during machining.